タイトル | Interdiffusion behavior of tungsten or rhenium and group 5 and 6 elements and alloys of the periodic table, part 1 |
本文(外部サイト) | http://hdl.handle.net/2060/19740025933 |
著者(英) | Arcella, F. G. |
著者所属(英) | Westinghouse Astronuclear Lab. |
発行日 | 1974-09-01 |
言語 | eng |
内容記述 | Arc cast W, CVD W, CVD Re, and powder metallurgy Re materials were hot isostatically pressure welded to ten different refractory metals and alloys (Cb, Cb-1Zr, Ta, Ta-10W, T-111, ASTAR-811C, W-25Re, Mo-50Re, W-30Re-20Mo, ect.) and thermally aged at 10 to the minus 8th power torr at 1200, 1500, 1630, 1800, and 2000 C for 100 to 2000 hours. Electron beam microprobe analysis was used to characterize the interdiffusion zone width of each couple system as a function of age time and temperature. Extrapolations of interdiffusion zone thickness to 10,000 hours were made. Classic interdiffusion analysis was performed for several of the systems by Boltzmann-Matano analysis. A method of inhibiting Kirkendall voids from forming during thermal ageing of dissimilar metal junctions was devised and experimentally demonstrated. An electron beam weld study of Cb-1Zr to Re and W-25Re demonstrated the limited acceptability of these welds. |
NASA分類 | MATERIALS, METALLIC |
レポートNO | 74N34046 NASA-CR-134490 WANL-M-FR-74-005-PT-1 |
権利 | No Copyright |
URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/192815 |
|