タイトル | Structural Transition and Magnetic Field Induced Strain in Ni50Mn26.5Ga23.5 Alloy |
DOI | info:doi/10.15017/14559 |
本文(外部サイト) | https://catalog.lib.kyushu-u.ac.jp/opac_download_md/14559/full-28-2-1.pdf |
参考URL | http://hdl.handle.net/2324/14559 |
著者(英) | Ngo Van, Nong; Ohtaki, Michitaka |
発行日 | 2009-05-16 |
発行機関など | 九州大学大学院総合理工学府 |
刊行物名 | 九州大学大学院総合理工学報告 |
巻 | 28 |
号 | 2 |
開始ページ | 237 |
終了ページ | 239 |
刊行年月日 | 2006-10 |
言語 | eng |
内容記述 | Polycrystalline samples of Ni50Mn26.5Ga23.5 were prepared by arc-melting method. The structural transformation from tetragonal to cubic was observed from X-ray diffraction analysis as a function of temperature in the temperature range from 100 K to 370 K. Thermal magnetization curves measured at a low magnetic field of 300 Oe showed a sharp structural transformation at TM = 260 K and a magnetic transition at Curie temperature TC = 375 K. Thermal expansions were investigated in the vicinity of TM after different cooling procedures: zero-field-cooling (ZFC) and field-cooling (FC). A magnetic-field-induced strain (MFIS) of ~ 0.2 % obtained from the difference between the ZFC and FC thermal expansions curves is remarkable. |
キーワード | Shape memory alloy; Martensite; Austenite; Twin variants |