| タイトル | Thermal emittance enhancement of graphite-copper composites for high temperature space based radiators |
| 本文（外部サイト） | http://hdl.handle.net/2060/19910020018 |
| 著者（英） | Rutledge, Sharon K.; Cooper, Jill M.; Forkapa, Mark J. |
| 著者所属（英） | NASA Lewis Research Center |
| 発行日 | 1991-01-01 |
| 言語 | eng |
| 内容記述 | Graphite-copper composites are candidate materials for space based radiators. The thermal emittance of this material, however, is a factor of two lower than the desired emittance for these systems of greater than or equal to 0.85. Arc texturing was investigated as a surface modification technique for enhancing the emittance of the composite. Since the outer surface of the composite is copper, and samples of the composite could not be readily obtained for testing, copper was used for optimization testing. Samples were exposed to various frequencies and currents of arcs during texturing. Emittances near the desired goal were achieved at frequencies less than 500 Hz. Arc current did not appear to play a major role under 15 amps. Particulate carbon was observed on the surface, and was easily removed by vibration and handling. In order to determine morphology adherence, ultrasonic cleaning was used to remove the loosely adherent material. This reduced the emittance significantly. Emittance was found to increase with increasing frequency for the cleaned samples up to 500 Hz. The highest emittance achieved on these samples over the temperature range of interest was 0.5 to 0.6, which is approximately a factor of 25 increase over the untextured copper emittance. |
| NASA分類 | NONMETALLIC MATERIALS |
| レポートNO | 91N29332
AIAA PAPER 91-3527
E-6475
NAS 1.15:105178
NASA-TM-105178 |
| 権利 | No Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/131313 |