| タイトル | Development of solid-lubricated ball-screws for use in space |
| 本文（外部サイト） | http://hdl.handle.net/2060/19910015303 |
| 著者（英） | Chiba, Masatoshi; Nishimura, Makoto; Gyougi, Toru; Seki, Katsumi |
| 著者所属（英） | Nissan Motor Co. Ltd. |
| 発行日 | 1991-05-01 |
| 言語 | eng |
| 内容記述 | Ball-screws lubricated by solid lubricant films containing molybdenum disulphide are developed. The ball-screws (shaft diameter: phi 25 mm, length: 667 mm) were operated under a load of 40 to 120 N at a speed of 1.5 to 200 rpm at 10(exp -5) Pa. First, ball-screws made of stainless steel SUS 440C were studied using test equipment originally designed for this study. To reduce weight, the next step taken was to develop a ball-screw made of 6Al-4V-titanium. Long wear-life of more than 1 x 10(exp 7) revolutions was achieved with solid lubricated ball-screws made of SUS 440C and 6Al-4V-titanium in a hard vacuum. According to the surface profile of the shaft measured after 1 x 10(exp 7) revolutions, more solid lubricant remained on the surface of 6Al-4V-titanium than that of stainless steel. Auger and EPMA analysis confirmed lubrication was maintained by solid lubricant on nuts and screws after the lubricant films on the balls were worn off. |
| NASA分類 | MECHANICAL ENGINEERING |
| レポートNO | 91N24617 |
| 権利 | No Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/132253 |
|