| タイトル | Composite materials for space applications |
| 本文（外部サイト） | http://hdl.handle.net/2060/19910009925 |
| 著者（英） | Wendt, Robert G.; Misra, Mohan S.; Rawal, Suraj P. |
| 著者所属（英） | Martin Marietta Aerospace |
| 発行日 | 1990-08-01 |
| 言語 | eng |
| 内容記述 | The objectives of the program were to: generate mechanical, thermal, and physical property test data for as-fabricated advanced materials; design and fabricate an accelerated thermal cycling chamber; and determine the effect of thermal cycling on thermomechanical properties and dimensional stability of composites. In the current program, extensive mechanical and thermophysical property tests of various organic matrix, metal matrix, glass matrix, and carbon-carbon composites were conducted, and a reliable database was constructed for spacecraft material selection. Material property results for the majority of the as-fabricated composites were consistent with the predicted values, providing a measure of consolidation integrity attained during fabrication. To determine the effect of thermal cycling on mechanical properties, microcracking, and thermal expansion behavior, approximately 500 composite specimens were exposed to 10,000 cycles between -150 and +150 F. These specimens were placed in a large (18 cu ft work space) thermal cycling chamber that was specially designed and fabricated to simulate one year low earth orbital (LEO) thermal cycling in 20 days. With this rate of thermal cycling, this is the largest thermal cycling unit in the country. Material property measurements of the thermal cycled organic matrix composite laminate specimens exhibited less than 24 percent decrease in strength, whereas, the remaining materials exhibited less than 8 percent decrease in strength. The thermal expansion response of each of the thermal cycled specimens revealed significant reduction in hysteresis and residual strain, and the average CTE values were close to the predicted values. |
| NASA分類 | COMPOSITE MATERIALS |
| レポートNO | 91N19238
NASA-CR-187472
NAS 1.26:187472
MCR-90-502 |
| 権利 | No Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/133715 |
|