タイトル | Microstructure: Property correlation |
本文(外部サイト) | http://hdl.handle.net/2060/19900019564 |
著者(英) | Jayaraman, N. |
著者所属(英) | Cincinnati Univ. |
発行日 | 1990-10-01 |
言語 | eng |
内容記述 | Strain controlled torsional and biaxial (tension-torsion) low cycle fatigue behavior of Waspaloy was studied at room temperature as a function of heat treatment. Biaxial tests were conducted under proportional (when the axial and torsional strain cycles are in-phase) and non-proportional (when the axial and torsional strain cycles are 90 deg out-of-phase) cyclic conditions. The deformation behavior under these different cyclic conditions were evaluated by slip trace analysis. For this, a Schmidt-type factor was defined for multiaxial loading conditions and it was shown that when the slip deformation is predominant, non-proportional cycles are more damaging than proportional or pure axial or torsional cycles. This was attributed to the fact that under non-proportional cyclic conditions, deformation was through multiple slip as opposed single slip for other loading conditions, which gave rise to increased hardening. The total life for a given test condition was found to be independent of heat treatment. This was interpreted as being due to the differences in the cycles to initiation and propagation of cracks. |
NASA分類 | STRUCTURAL MECHANICS |
レポートNO | 90N28880 NASA-CR-180406 NAS 1.26:180406 |
権利 | No Copyright |
URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/136223 |
|