| タイトル | Overlay coating degradation by simultaneous oxidation and coating/substrate interdiffusion |
| 本文（外部サイト） | http://hdl.handle.net/2060/19840023274 |
| 著者（英） | Nesbitt, J. A. |
| 著者所属（英） | NASA Lewis Research Center |
| 発行日 | 1983-08-01 |
| 言語 | eng |
| 内容記述 | Degradation of NiCrAlZr overlay coatings on various NiCrAl substrates was examined after cyclic oxidation. Concentration/distance profiles were measured in the coating and substrate after various oxidation exposures at 1150 C. For each stubstrate, the Al content in the coating decreased rapidly. The concentration/distance profiles, and particularly that for Al, reflected the oxide spalling resistance of each coated substrate. A numerical model was developed to simulate diffusion associated with overlay-coating degradation by oxidation and coating/substrate interdiffusion. Input to the numerical model consisted of the Cr and Al content of the coating and substrate, ternary diffusivities, and various oxide spalling parameters. The model predicts the Cr and Al concentrations in the coating and substrate after any number of oxidation/thermal cycles. The numerical model also predicts coating failure based on the ability of the coating to supply sufficient Al to the oxide scale. The validity of the model was confirmed by comparison of the predicted and measured concentration/distance profiles. The model was subsequently used to identify the most critical system parameters affecting coating life. |
| NASA分類 | METALLIC MATERIALS |
| レポートNO | 84N31344
NASA-TM-83738
NAS 1.15:83738
E-2223 |
| 権利 | No Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/158694 |