| タイトル | Creep fatigue of low-cobalt superalloys: Waspalloy, PM U 700 and wrought U 700 |
| 本文（外部サイト） | http://hdl.handle.net/2060/19840005197 |
| 著者（英） | Hopper, A. T.; Leis, B. N.; Rungta, R. |
| 著者所属（英） | Battelle Columbus Labs. |
| 発行日 | 1983-09-01 |
| 言語 | eng |
| 内容記述 | The influence of cobalt content on the high temperature creep fatigue crack initiation resistance of three primary alloys was evaluated. These were Waspalloy, Powder U 700, and Cast U 700, with cobalt contents ranging from 0 up to 17 percent. Waspalloy was studied at 538 C whereas the U 700 was studied at 760 C. Constraints of the program required investigation at a single strain range using diametral strain control. The approach was phenomenological, using standard low cycle fatigue tests involving continuous cycling tension hold cycling, compression hold cycling, and symmetric hold cycling. Cycling in the absence of or between holds was done at 0.5 Hz, whereas holds when introduced lasted 1 minute. The plan was to allocate two specimens to the continuous cycling, and one specimen to each of the hold time conditions. Data was taken to document the nature of the cracking process, the deformation response, and the resistance to cyclic loading to the formation of small cracks and to specimen separation. The influence of cobalt content on creep fatigue resistance was not judged to be very significant based on the results generated. Specific conclusions were that the hold time history dependence of the resistance is as significant as the influence of cobalt content and increased cobalt content does not produce increased creep fatigue resistance on a one to one basis. |
| NASA分類 | METALLIC MATERIALS |
| レポートNO | 84N13265
NASA-CR-168260
NAS 1.26:168260 |
| 権利 | No Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/160939 |
|