| タイトル | Crosslinking Amine-Modified Silica Aerogels with Epoxies: Mechanically Strong Lightweight Porous Materials |
| 本文（外部サイト） | http://hdl.handle.net/2060/20050123913 |
| 著者（英） | Johnston, J. Chris; Meador, Mary Ann B.; Zhang, Guo-Hui; Vassilaras, Plousia; Leventis, Nicholas; Ilhan, Faysal; Fabrizio, Eve F.; Dass, Amala |
| 著者所属（英） | NASA Glenn Research Center |
| 発行日 | 2005-01-01 |
| 言語 | eng |
| 内容記述 | The mesoporous surfaces of TMOS-derived silica aerogels have been modified with amines by co-polymerization of TMOS with APTES. The amine sites have become anchors for crosslinking the nanoparticles of the skeletal backbone of the aerogel by attachment of di-, tri and tetra-functional epoxies. The resulting conformal coatings increase the density of the native aerogels by a factor of 2-3 but the strength of the resulting materials may increase by more than two orders of magnitude. Processing variables such as amount of APTES used to make the gels, the epoxy type and concentration used for crosslinking, as well as the crosslinking temperature and time were varied according to a multivariable design-of-experiments (DOE) model. It was found that while elastic modulus follows a similar trend with density, maximum strength is attained neither at the maximum density nor at the highest concentration of -NH2 groups, suggesting surface saturation effects. Aerogels crosslinked with the tri-functional epoxide always show improved strength compared with aerogels crosslinked with the other two epoxides under identical conditions. Solid C-13 NMR studies show residual unreacted epoxides, which condense with ne another by heating crosslinked aerogels at 150 C. |
| NASA分類 | Inorganic, Organic and Physical Chemistry |