| 内容記述 | The effects are assessed of TiB2 reinforcement and parent alloy Li content on the weldability of Weldalite (tm) 049 type alloys. Welding trials were performed using either AC or DC polarity gas tungsten arc (GTA) welding according to described procedures. The welding was performed under conditions of high restraint on 5 cm (2 in) wide x 25.4 cm (10 in) long plates machined from the 0.952 cm (0.375 in) extruded bar parallel to the extrusion direction. A 37.5 deg bevel was machined on the center edge of the extruded bar. Cut rod filler wire was machined from three alloys, and one commercially available 2319 filler wire was also used. The preliminary assessment of the weldability revealed no propensity for hot cracking under conditions of high restraint. This result is significant, because hot cracking has been reported for all other leading aluminum lithium alloys welded with certain conventional filler alloys. The strengths for Weldalite parent welded with parent filler obtained were higher than those for alloys used in launch systems, such as 2219 and 2014 welded with 2319 and 4043 fillers, respectively. Even higher values were obtained by variable polarity plasma arc welding (e.g., 54 ksi (372 MPa) mean tensile strength). |