| タイトル | Formation of Minor Phases in a Nickel-Based Disk Superalloy |
| 本文（外部サイト） | http://hdl.handle.net/2060/20120013217 |
| 著者（英） | Garg, A.; Sudbrack, C. K.; Rogers, R. B.; Miller, D. R.; Johnson, D.; Hull, D. R.; Gayda, J.; Gabb, T. P.; Semiatin, S. L. |
| 著者所属（英） | NASA Glenn Research Center |
| 発行日 | 2012-07-23 |
| 言語 | eng |
| 内容記述 | The minor phases of powder metallurgy disk superalloy LSHR were studied. Samples were consistently heat treated at three different temperatures for long times to approximate equilibrium. Additional heat treatments were also performed for shorter times, to then assess non-equilibrium conditions. Minor phases including MC carbides, M23C6 carbides, M3B2 borides, and sigma were identified. Their transformation temperatures, lattice parameters, compositions, average sizes and total area fractions were determined, and compared to estimates of an existing phase prediction software package. Parameters measured at equilibrium sometimes agreed reasonably well with software model estimates, with potential for further improvements. Results for shorter times representing non-equilibrium indicated significant potential for further extension of the software to such conditions, which are more commonly observed during heat treatments and service at high temperatures for disk applications. |
| NASA分類 | Aircraft Propulsion and Power |
| レポートNO | E-18185
NASA/TM-2012-217604 |
| 権利 | Copyright, Distribution as joint owner in the copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/241578 |
|