| タイトル | AC Electric Field Activated Shape Memory Polymer Composite |
| 本文（外部サイト） | http://hdl.handle.net/2060/20110015327 |
| 著者（英） | Siochi, Emilie J.; Turner, Travis L.; Kang, Jin Ho; Penner, Ronald K. |
| 著者所属（英） | NASA Langley Research Center |
| 発行日 | 2011-08-28 |
| 言語 | eng |
| 内容記述 | Shape memory materials have drawn interest for applications like intelligent medical devices, deployable space structures and morphing structures. Compared to other shape memory materials like shape memory alloys (SMAs) or shape memory ceramics (SMCs), shape memory polymers (SMPs) have high elastic deformation that is amenable to tailored of mechanical properties, have lower density, and are easily processed. However, SMPs have low recovery stress and long response times. A new shape memory thermosetting polymer nanocomposite (LaRC-SMPC) was synthesized with conductive fillers to enhance its thermo-mechanical characteristics. A new composition of shape memory thermosetting polymer nanocomposite (LaRC-SMPC) was synthesized with conductive functionalized graphene sheets (FGS) to enhance its thermo-mechanical characteristics. The elastic modulus of LaRC-SMPC is approximately 2.7 GPa at room temperature and 4.3 MPa above its glass transition temperature. Conductive FGSs-doped LaRC-SMPC exhibited higher conductivity compared to pristine LaRC SMP. Applying an electric field at between 0.1 Hz and 1 kHz induced faster heating to activate the LaRC-SMPC s shape memory effect relative to applying DC electric field or AC electric field at frequencies exceeding1 kHz. |
| NASA分類 | Composite Materials |
| レポートNO | NF1676L-12475 |
| 権利 | Copyright, Distribution as joint owner in the copyright |
|