| タイトル | Fracture Mechanics Analysis of LH2 Feed Line Flow Liners |
| 本文（外部サイト） | http://hdl.handle.net/2060/20060020274 |
| 著者（英） | James, Mark A.; Raju, Ivatury S.; Elliott, Kenny B.; Brzowski, Matthew B.; Dawicke, David S.; Harris, Charles E. |
| 著者所属（英） | NASA Langley Research Center |
| 発行日 | 2006-01-01 |
| 言語 | eng |
| 内容記述 | Inspections of the Space Shuttle Main Engine revealed fatigue cracks growing from slots in the flow liner of the liquid hydrogen (LH2) feed lines. During flight, the flow liners experience complex loading induced by flow of LH2 and the resonance characteristics of the structure. The flow liners are made of Inconel 718 and had previously not been considered a fracture critical component. However, fatigue failure of a flow liner could have catastrophic effect on the Shuttle engines. A fracture mechanics study was performed to determine if a damage tolerance approach to life management was possible and to determine the sensitivity to the load spectra, material properties, and crack size. The load spectra were derived separately from ground tests and material properties were obtained from coupon tests. The stress-intensity factors for the fatigue cracks were determined from a shell-dynamics approach that simulated the dominant resonant frequencies. Life predictions were obtained using the NASGRO life prediction code. The results indicated that adequate life could not be demonstrated for initial crack lengths of the size that could be detected by traditional NDE techniques. |
| NASA分類 | Spacecraft Propulsion and Power |
| レポートNO | AIAA Paper 2006-1782 |
| 権利 | Copyright, Distribution as joint owner in the copyright |
|