| タイトル | Thermally Conductive Metal-Tube/Carbon-Composite Joints |
| 本文（外部サイト） | http://hdl.handle.net/2060/20110020526 |
| 著者（英） | Copeland, Robert J. |
| 著者所属（英） | TDA Research, Inc. |
| 発行日 | 2004-09-01 |
| 言語 | eng |
| 内容記述 | An improved method of fabricating joints between metal and carbon-fiber-based composite materials in lightweight radiators and heat sinks has been devised. Carbon-fiber-based composite materials have been used in such heat-transfer devices because they offer a combination of high thermal conductivity and low mass density. Metal tubes are typically used to carry heat-transfer fluids to and from such heat-transfer devices. The present fabrication method helps to ensure that the joints between the metal tubes and the composite-material parts in such heat-transfer devices have both (1) the relatively high thermal conductances needed for efficient transfer of heat and (2) the flexibility needed to accommodate differences among thermal expansions of dissimilar materials in operation over wide temperature ranges. Techniques used previously to join metal tubes with carbon-fiber-based composite parts have included press fitting and bonding with epoxy. Both of these prior techniques have been found to yield joints characterized by relatively high thermal resistances. The present method involves the use of a solder (63 percent Sn, 37 percent Pb) to form a highly thermally conductive joint between a metal tube and a carbon-fiber-based composite structure. Ordinarily, the large differences among the coefficients of thermal expansion of the metal tube, solder, and carbon-fiber-based composite would cause the solder to pull away from the composite upon post-fabrication cooldown from the molten state. In the present method, the structure of the solder is modified (see figure) to enable it to deform readily to accommodate the differential thermal expansion. |
| NASA分類 | Man/System Technology and Life Support |
| レポートNO | MSC-22907 |
| 権利 | Copyright, Distribution as joint owner in the copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/268815 |
|