Domain structure of gamma Al2O3

Abstract

The single crystals of gamma Al2O3 obtained by heating single crystals of gibbsite Al(OH)3 were studied by synchrotron radiation and under electron microscope. The diffraction patterns of single crystals of gamma Al2O3 show two different type of diffraction spots; one shows isotropic broadening and the other is sharp and shows streak of powder lines. The different features of two type of diffraction spots indicate that they are from different parts of the gamma Al2O3 crystal. The electron diffraction patterns of gamma Al2O3 obtained by the same heating procedure show only broadened spots and no sharp diffraction spots were observed in this study. Both results of X-ray and electron diffraction indicate that the bulk of gamma Al2O3 consist of two domains.

ギブサイトAl(OH)3の単結晶を加熱して得たγ-Al2O3の単結晶をシンクロトロン放射と電子顕微鏡により研究した。γ-Al2O3の単結晶の回折パターンは異なる2種類の回折スポットを示した。ひとつは等方性広がりを示し、他は鋭く、また粉末線の縞を示した。2種の回折スポットの特徴が異なるのは、回折スポットが別々のγ-Al2O3結晶部分から出ていることを示している。本研究では、同一の加熱手法で得たγ-Al2O3の電子回折パターンは、広がったスポットだけを示し、鋭い回折スポットは観測しなかった。X線と電子回折の両結果はγ-Al2O3のバルクが2つの分域から成ることを示している。