| タイトル | In situ Pulsed Laser Deposition of C-Axis Oriented MgB2 Films and Their Characterization |
| 著者（英） | Venkatesan, T.; Ogale, S. B.; Kulkarni, V. N.; Kale, S. N.; Lakew, Brook; Shinde, Sanjay |
| 著者所属（英） | NASA Goddard Space Flight Center |
| 発行日 | 2004-02-01 |
| 言語 | eng |
| 内容記述 | The recent discovery of an intermetallic superconductor MgB2 has renewed interest in the area of superconductivity not only because of fundamental understanding of superconductivity but also due to its potential applicability in devices such as thermal detectors. Considerable amount of research has been devoted to obtain MgB2 films by an all in situ growth technique. We have grown MgB2 thin films by an all in situ pulsed laser deposition process from pure B and Mg targets. Ultrathin layers of B and Mg were deposited in a multilayer configuration. Hundreds of such Mg-B bilayers with a capping Mg layer on the top were deposited on sapphire substrate. These depositions were done in high vacuum (approx. 10(exp -7) Torr) and at room temperature. After deposition, such a configuration was annealed at high temperature for a short time in a forming gas (4% H2 in Ar). The best films, obtained by this procedure, showed superconducting transition temperature approx. 30 K. These films have been characterized by x-ray diffraction, Rutherford Backscattering Spectrometry, AC susceptibility-, resistivity- (with and without magnetic field) and 1/f noise-measurements. The physical properties of these films will be presented and discussed. |
| NASA分類 | Solid-State Physics |
| 権利 | No Copyright |
|