| タイトル | Predicting the oxidative lifetime of beta NiAl-Zr alloys |
| 著者（英） | Vinarcik, E. J.; Nesbitt, J. A. |
| 著者所属（英） | NASA Lewis Research Center |
| 発行日 | 1991-01-01
1991 |
| 言語 | eng |
| 内容記述 | Nickel aluminides containing 40 to 50 at. pct Al and 0.1 at. pct Zr were studied following cyclic oxidation at 1400 C. The selective oxidation of Al resulted in the formation of protective Al2O3 scales on each alloy composition. However, repeated cycling eventually resulted in the gradual formation of less-protective NiAl2O4, first appearing on the 40Al alloys followed at longer times on the 45Al alloys. The appearance of the NiAl2O4, signaling the end of the protective scale-forming capability of the alloy, was related to the presence of gamma-prime (Ni3Al) which formed as a result of the loss of Al from the sample. A diffusion model, based on finite-difference techniques, was developed to predict the protective life of beta Ni-Al alloys. This model predicts Ni and Al concentration profiles after various oxidation exposures. The model can predict the oxidative lifetime due to Al depletion when the Al concentration decreases to a critical concentration. Measured Al concentration profiles on two alloys after various oxidation exposures are compared to those predicted by the diffusion model. The time to the appearance of the NiAl2O4 and that predicted by the diffusion model are compared and discussed. |
| NASA分類 | METALLIC MATERIALS |
| レポートNO | 93A53939 |
| 権利 | Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/314231 |
|