| タイトル | Properties of hybrid CVD/PAN graphite fibers and their bromine intercalation compounds |
| 著者（英） | Marabito, Mark; Moinuddin, Alia; Lake, Max L.; Gaier, James R. |
| 著者所属（英） | NASA|NASA Lewis Research Center |
| 発行日 | 1992-01-01
1992 |
| 言語 | eng |
| 内容記述 | A hybrid fiber with a PAN core surrounded by a vapor grown carbon fiber (VGCF) sheath was fabricated using a proprietary process. The density, ultimate tensile strength, Young's modulus, and resistivity of pristine and bromine intercalated fibers made by this technique having diameters varying from 5 to 50 microns were compared with the values predicted from the rule of mixtures model. For both the pristine and intercalated fibers, the density, ultimate tensile strength, and Young's modulus of the fibers were lower than predicted, but the resistivity was measured to be consistent with predictions. The lower than theoretical mechanical properties may be evidence of a low density disordered interface between the core and the sheath which would lower the density and degrade the mechanical properties, but would leave the resistivity nearly unaffected. Intercalation had little if any effect on the ultimate tensile strength and Young's modulus, but raised the density by about 11 pct., and lowered the resistivity by an order of magnitude. The diameter dependence of the resistivity showed evidence of a depletion layer of the type found in VGCF. |
| NASA分類 | COMPOSITE MATERIALS |
| レポートNO | 93A17675 |
| 権利 | Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/321753 |
|