| タイトル | Fatigue crack propagation behavior of a single crystalline superalloy |
| 著者（英） | Lerch, B. A.; Antolovich, Stephen D. |
| 著者所属（英） | Georgia Inst. of Tech.|NASA Lewis Research Center |
| 発行日 | 1990-08-01 |
| 言語 | eng |
| 内容記述 | Crack propagation mechanisms occurring at various temperatures in a single crystalline Ni-base alloy, Rene N4, were investigated. The rates of crack growth at 21, 704, 927, 1038, and 1093 C were measured in specimens with 001-line and 110-line directions parallel to the load axis and the machined notch, respectively, using a pulsed dc potential drop apparatus, and the fracture surfaces at each temperature were examined using SEM. Crack growth rates (CGRs) for specimens tested at or below 927 C were similar, while at two higher temperatures, the CGRs were about an order of magnitude higher than at the lower temperatures. Results of SEM observations showed that surface morphologies depended on temperature. |
| NASA分類 | METALLIC MATERIALS |
| レポートNO | 90A48635 |
| 権利 | Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/354077 |
|