| タイトル | Oxidation behavior of FeAl+Hf,Zr,B |
| 著者（英） | Smialek, James L.; Gaydosh, Darrell J.; Doychak, Joseph |
| 著者所属（英） | NASA Lewis Research Center |
| 発行日 | 1989-01-01 |
| 言語 | eng |
| 内容記述 | The oxidation behavior of Fe-40Al-1Hf, Fe-40Al-1Hf-0.4B, and Fe-40Al-0.1Zr-0.4B (at. percent) alloys was characterized after 900, 1000, and 100 C exposures. Isothermal tests revealed parabolic kinetics after a period of transitional theta-alumina scale growth. The parabolic growth rates for the subsequent alpha-alumina scales were about five times higher than those for NiAl+0.1Zr alloys. The isothermally grown scales showed a propensity toward massive scale spallation due to both extensive rumpling from growth stresses and to an inner layer of Hf02. Cyclic oxidation for 200 1-hr cycles produced little degradation at 900 or 1000 C, but caused significant spallation at 1100 C in the form of small segments of the outer scale. The major difference in the cyclic oxidation of the three FeAl alloys was increased initial spallation for FeAl+Zr,B. Although these FeAl alloys showed many similarities to NiAl alloys, they were generally less oxidation resistant. It is believed that this resulted from nonoptimal levels of dopants and larger thermal expansion mismatch stresses. |
| NASA分類 | METALLIC MATERIALS |
| レポートNO | 90A24858 |
| 権利 | Copyright |
|