| タイトル | Yielding and deformation behavior of the single crystal superalloy PWA 1480 |
| 著者（英） | Milligan, Walter W.; Antolovich, Stephen D. |
| 著者所属（英） | Georgia Inst. of Tech. |
| 発行日 | 1987-01-01 |
| 言語 | eng |
| 内容記述 | Interrupted tensile tests were conducted to fixed plastic strain levels in 100 ordered single crystals of the nickel based superalloy PWA 1480. Testing was done in the range of 20 to 1093 C, at strain rate of 0.5 and 50 percent/min. The yield strength was constant from 20 to 760 C, above which the strength dropped rapidly and became a strong function of strain rate. The high temperature data were represented very well by an Arrhenius type equation, which resulted in three distinct temperature regimes. The deformation substructures were grouped in the same three regimes, indicating that there was a fundamental relationship between the deformation mechanisms and activation energies. Models of the yielding process were considered, and it was found that no currently available model was fully applicable to this alloy. It was also demonstrated that the initial deformation mechanism (during yielding) was frequently different from that which would be inferred by examining specimens which were tested to failure. |
| NASA分類 | METALLIC MATERIALS |
| レポートNO | 87A32040 |
| 権利 | Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/378854 |
|