| タイトル | The effects of biaxial loading on the fracture characteristics of several engineering materials |
| 著者（英） | Liebowitz, H.; Poulose, P. K.; Jones, D. L. |
| 著者所属（英） | George Washington Univ. |
| 発行日 | 1986-01-01 |
| 言語 | eng |
| 内容記述 | Using the George Washington University biaxial test system, a static fracture toughness study of two polymers (PMMA and PVC) and three aluminum alloys was performed for several variations in specimen geometry. Photoelastic experiments indicate that the applied load biaxiality has a very strong influence on the size and shape of the crack-tip stress field, and fracture toughness values for both polymers were seen to decrease with increasing load biaxiality. The load biaxiality was also found to have a strong influence on the crack growth direction in PMMA and a negligible influence on the PVC. The 7075-T6 aluminum toughness values increased with biaxiality, while intermediate peak toughness values were noted at a 0.5 biaxiality ratio for the more ductile 2024-T3 and 6061-T4 alloys. Fracture toughnesses at the highest biaxiality ratios were found to be equal to the uniaxial results. |
| NASA分類 | STRUCTURAL MECHANICS |
| レポートNO | 86A44911 |
| 権利 | Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/383551 |
|