Effect of curvature on fillet formation during aluminum brazing

Abstract

Effect of curvature of convex and concave planes on the fillet size formed after brazing of aluminum was investigated in relation to the brazing method. The fillet size was measured by throat thickness and vertical leg length on the inside (concave plane) and outside (convex) plane of an aluminum pipe braze specimen. Fillet size estimated by the Laplace equation was larger on the inside than that on the outside. In vacuum brazing inside fillet was larger than outside one under limited test conditions, while in dip brazing inside fillet was always larger than outside one, which agreed well with the prediction of the Laplace equation. The discrepancy between the calculation and experimental results in vacuum brazing was attributed to the poor flowability of molten filler metal.

アルミニウムろう付後に形成されるすみ肉の大きさに及ぼす凸面および凹面の湾曲の影響を、ろう付法との関連において検討した。すみ肉の大きさは、アルミニウム管ろう付試験片の内面(凹面)および外面(凸面)の、のど厚と垂直脚長を測定して求めた。ラプラス方程式から推定したすみ肉の大きさは、限定試験条件下での外側のそれより大きかったが、一方、深くろう付した内部すみ肉は、常に外側のすみ肉より大きかった。これは、ラプラス方程式からの予測とよく一致した。真空ろう付での計算結果と実験結果との食違いは、溶融溶加剤の流動性不良に起因するものであった。