Technical Report of ISSP Ser. A: Number 2812

Abstract

The composition ranges of the Al-Ni-Co decagonal quasicrystals in the ordered and disordered states have been investigated. All the decagonal phases in the 650 C-annealed samples examined were in the ordered state, while that in each 850 C-annealed sample was either in a partially ordered state or in the completely disordered state. From these results, compositional dependence of the order-disorder transformation temperature is estimated. The ordered and disordered structures have been observed by high resolution electron microscopy. The arrangements of ring-like contrasts in the images have been analyzed based on a high-dimensional description of the quasicrystalline structure. Electrical resistivity measured for a single-grain decagonal phase has exhibited large anisotropy: the resistivity along a direction perpendicular to the tenfold axis (c(sub perp)) is about seven times larger than that along the tenfold direction (c(sub para)). Magnetoresistance with the current along c(sub perp) under the magnetic field in two different directions has shown no appreciable anisotropy.

秩序および無秩序状態のAl-Ni-co 10角形準結晶の組成範囲を調べた。650度Cで焼きなました試料のすべては秩序化された状態であったが、850度Cで焼きなました試料は部分的に秩序化された状態か完全に無秩序の状態であるかのいずれかであった。これらの結果から秩序-無秩序転移温度の組成依存性を調べた。秩序および無秩序構造を高分解電子顕微鏡により観察した。像のリング状コントラストの配列を準結晶構造の高次元記述に基づいて解析した。単独の結晶粒の10角形の相について測定した電気抵抗率は大きな非等方性を示した。すなわち10軸(Cperp)に垂直な方向に沿った抵抗率は10方向(Cpara)に沿った抵抗率の約7倍の値を示した。2つの異なった方向を持つ磁場の下で、Cperpに沿った電流による磁気抵抗は感知できる異方性はまったく示さなかった。