| タイトル | Interdiffusion and intrinsic diffusion in the NiAl /delta/ phase of the Al-Ni system |
| 著者（英） | Seigle, L. L.; Shankar, S. |
| 著者所属（英） | Howmet Turbine Components Corp.|State Univ. of New York |
| 発行日 | 1978-10-01 |
| 言語 | eng |
| 内容記述 | Interdiffusion coefficients at 950 to 1150 C and the ratio of intrinsic diffusion coefficients at 1100 C were measured as functions of composition in the NiAl (delta) phase of the Al-Ni system, using a vapor-solid technique. Diffusivity values were also obtained for the Ni3Al (epsilon) and Ni (Al) solid solution (zeta) phases from 950 to 1150 C. The interdiffusion coefficient in NiAl (delta) varies several orders of magnitude over the delta phase field with a deep minimum in the diffusivity-composition curve at 48 to 49 at% Al. The ratio of intrinsic diffusion coefficients DNi/DAl, in the delta phase also varies with composition from a value of 3 to 3.5 below 50 at% Al to 0.1 or less above 50 at% Al. |
| NASA分類 | METALLIC MATERIALS |
| レポートNO | 79A11942 |
| 権利 | Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/429671 |