| タイトル | The role of grain size and shape in strengthening of dispersion hardened nickel alloys. |
| 著者（英） | Clauer, A. H.; Wilcox, B. A. |
| 発行日 | 1972-05-01 |
| 言語 | eng |
| 内容記述 | Thermomechanical processing was used to develop various microstructures in Ni, Ni-2ThO2, Ni-20Cr, Ni-20Cr-2ThO2, Ni-20Cr-10W and Ni-20Cr-10W-2ThO2, and the influence of microstructure on room temperature and elevated temperature strength was investigated. The yield strength at 25 C increased with substructure refinement according to the Hall-Petch relation. It was found that substructure refinement was a much more potent means of strengthening at room temperature than was dispersion hardening. At elevated temperature (1093 C), the most important microstructural feature affecting strength of dispersion hardened nickel alloys was the grain aspect ratio, i.e. grain length, L, divided by grain width,l. The yield strength and creep strength increased linearly with increasing L/l. |
| NASA分類 | MATERIALS, METALLIC |
| レポートNO | 72A30368 |
| 権利 | Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/462110 |
|