Technical Report of ISSP Ser. A: Number 2971

Abstract

It is reported that the intermetallic compound CeFeGe3 is a new Kondo compound possessing a stable valency and a very high Kondo temperature of the order of 100 K. The magnetic susceptibility chi showed Curie-Weiss behavior above about 200 K and the Weiss temperature was found to be about -90 K. Chi saturates at the lowest temperatures after making a faint maximum around 50 K. Below 8 K the specific heat exhibited a large temperature independent linear term gamma, amounting to 150 mJ/mol･K(exp 2) and the electrical resistivity showed T(sub 2)-dependence below about 4 K. The compound exhibited no phase transitions above 0.05 K and it is characterized as a nonmagnetic heavy-electron compound with the properties of a heavy Fermi liquid at low temperatures. The results of magnetic susceptibility and magnetic contribution of specific heat suggest a j = 3/2 Kondo effect, which is also consistent with the result of thermoelectric power.

金属間化合物CeFeGe3が安定な原子価と100Kオーダの非常に高い近藤温度を持つ新しい近藤化合物であることを報告する。帯磁率は200K以上でキュリー･ワイス挙動を示し、ワイス温度は約-90Kであった。帯磁率は50K近傍で緩やかな極値を作った後最低温度で飽和した。8K以下で比熱は150mJ/mol･K{2}という温度に独立な大きな1次の項を示し、電気抵抗率は4K以下で温度の2乗依存性を示した。この化合物は0.05K以上では相転移を示さず低温で重いフェルミ液体の性質を持つ非磁性の重い電子化合物として特徴づけられる。帯磁率と比熱の磁気的寄与についての結果はj=3/2の近藤効果を示唆している。これは熱電能の結果とも矛盾しない。