KEK Report: 96-7

Abstract

A study on the effect of beams on the ferrite absorber was performed using Tristan MR (Main Ring). The tested absorber consists of a 300 mm-diam. copper pipe with 4 mm-thick ferrite inner layer, which was fabricated with Hot Isostatic Press (HIP) technique. No spark, damage, or degradation were observed up to the highest available single bunch current of 4.4 mA, i.e. 2.8 x 10(exp 11) electrons per bunch, which is 8.5 times higher than that of KEKB (B factory of National Laboratory for High Energy Physics) low energy ring. The loss factor showed significant increase with bunch shortening, e.g. 2.6 V/pC at 4 mm was about 40 percent higher than the value predicted by the calculation assuming Gaussian bunch and no incoming power from outside of the chamber.

フェライト吸収体へのビームの効果の研究を、トリスタンMRを用いて行った。試験した吸収体は、4mm厚のフェライトの内側層のある直径300mmの銅製のパイプからなり、熱間静水圧成形（HIP）技術により作成したものである。スパーク、損傷および劣化は、単バンチ電流の最高出力である4.4mA、すなわちバンチ当たり2.8×10{11}電子まで全く観察されることなく、この値はKEKB(高エネルギー物理学研究所Bファクトリ)の値より8.5倍高いものである。損失率は、バンチ長が短くなるに従って急激に増加し、例えば4mmで2.6V/pCという値は、ガウス型バンチと、チャンバー外部からの入力電源がないと仮定して計算した予測値より約40パーセント高くなった。