Technical Report of ISSP Ser. A: Number 3076

Abstract

A gradual change from Kondo lattice to impurity Kondo regime has been observed in Ce(1-x)La(x)FeGe3 (x = 0, 0.1, 0.3, 0.5, 1.0). CeFeGe3 reveals a very much reduced resistivity below about 100 K corresponding to the coherent state of Kondo lattice. Ce(0.5)La(0.5)FeGe3, on the other hand, shows a resistance minimum around 30 K which is consistent with the impurity Kondo regime. The ground state of CeFeGe3 turns out to be very stable against the La substitution and no magnetic instability is induced in the present diluted system. Magnetic susceptibility at 0 K per Ce mole, chi(0), and the linear term of the specific heat, gamma, increase by 24 percent and 15 percent from x = 0.0 to 0.5, respectively. The Kondo temperatures T(sub k)'s estimated from chi(0) and gamma accordingly decrease by 20 and 13 percent in the same range of La content. This decrease of T(sub k) is explained by the lattice expansion caused by the substitution of La for Ce.

Ce(1-x)La(x)FeGe3(x=0,0.1,0.3,0.5,1.0)においてKondo格子から不純物Kondoレジームへの緩やかな変化を観測した。CeFeGe3は約100K以下で抵抗の激減を示すが、これはKondo格子のコヒーレント状態に相当する。一方、Ce(0.5)La(0.5)FeGe3は30K近辺で最小の抵抗値を示すが、これは不純物Kondoレジームと一致している。CeFeGe3の基底状態はLaの置換に対して極めて安定であることが分り、また、この希薄系では磁気不安定性が誘導されないことが分った。0KでのCeモル当りの磁化率Χ(0)および比熱の線形項γはX=0.0から0.5までそれぞれ24%および15%増大する。Χ(0)およびγから予測されるKondo温度TKは同じ範囲のLa含有量で20%および13%減少する。このTKの減少はCeからLaの置換による格子展開によって説明できる。