タイトル | Au Colloids Formed by Ion Implantation in Muscovite Mica Studied by Vibrational and Electronic Spectroscopes and Atomic Force Microscopy |
本文(外部サイト) | http://hdl.handle.net/2060/20010000483 |
著者(英) | Tung, Y. S.; White, C. W.; Ueda, A.; Zhu, Jane G.; Zuhr, R. A.; Collins, W. E.; Henderson, D. O.; Mu, R. |
著者所属(英) | Fisk Univ. |
発行日 | 1997-02-01 |
言語 | eng |
内容記述 | Au was implanted into the (001) surface of Muscovite mica at an energy of 1.1 MeV and at doses of 1, 3, 6, and 10 x 10(exp 16) ions/cu cm. Optical spectra of the as-implanted samples revealed a peak at 2.28 eV (545 nm) which is attributed to the surface plasmon absorption of Au colloids. The infrared reflectance measurements show a decreasing reflectivity with increasing ion dose in the Si-O stretching region (900-1200 /cm). A new peak observed at 967 /cm increases with the ion dose and is assigned to an Si-O dangling bond. Atomic force microscopy images of freshly cleaved samples implanted with 6 and 10 x 10(exp 16) ions/sq cm indicated metal colloids with diameters between 0.9- 1.5 nm. AFM images of the annealed samples showed irregularly shaped structures with a topology that results from the fusion of smaller colloids. |
NASA分類 | Solid-State Physics |
レポートNO | URC97124 |
権利 | No Copyright |
|