| タイトル | Proof Test Diagrams for a Lithia-Alumina-Silica Glass-Ceramic |
| 著者（英） | Tucker, Dennis S. |
| 著者所属（英） | NASA Marshall Space Flight Center |
| 発行日 | 2003-01-01 |
| 言語 | eng |
| 内容記述 | The glass-ceramic (Zerodur, Schott Glaswerke, Mainz, Germany) contains 70% to 78% by weight crystalline phase of high-quartz structure with a mean crystal size of 50-55 nm. The vitreous phase has a positive thermal expansion coefficient which is practically balanced by the negative coefficient of the crystalline phase. This results in a material which can maintain longitudinal stability during thermal cycling. This was one of the reasons for its choice as the material for the grazing incidence mirrors for the Chandra X-Ray Facility. Brittle materials such as glass and glass-ceramics which exhibit slow crack growth and subsequent fast fracture to failure exhibit a time dependence in strength. The decrease in strength for a constant applied load is known as static fatigue. In many cases, environment plays a major role in the material lifetime. It has been shown for silicate glasses that crack velocity will increase as the amount of water vapor in the environment surface finish and rate of loading. A rough surface finish leads to a lower tensile strength than for an optically polished surface. The strength of glass is observed in general to increase with increasing load rate. This phenomena is known as dynamic fatigue. This was observed for Zerodur by Tucker and Gent and Tucker in previous dynamic fatigue studies, in which lifetimes were obtained. All of the above named factors need to be considered when glass is to be used in load bearing applications. |
| NASA分類 | Chemistry and Materials (General) |
| 権利 | No Copyright |
|