| タイトル | アルミナ繊維の微構造に及ぼす熱処理の影響 |
| その他のタイトル | Influence of heat treatment on microstructure of alumina fiber |
| 著者（日） | 岩永 浩 |
| 著者（英） | Iwanaga, Hiroshi |
| 著者所属（日） | 長崎大学 工学部 材料工学科 |
| 著者所属（英） | Nagasaki University Department of Materials Science and Engineering, Faculty of Engineering |
| 発行日 | 1999-01 |
| 刊行物名 | 長崎大学工学部研究報告
Reports of the Faculty of Engineering, Nagasaki University |
| 巻 | 29 |
| 号 | 52 |
| 開始ページ | 145 |
| 終了ページ | 151 |
| 刊行年月日 | 1999-01 |
| 言語 | jpn |
| 抄録 | The microstructural evolution of high purity alpha-alumina fiber (ALMAX) during sintering was analyzed. The structure of alumina grains changed into the alpha-phase through the intermediate delta, gamma and kappa phase during sintering. High content pores were found in alpha-phase grains by SEM (Scanning Electron Microscope) and TEM (Transmission Electron Microscope) observations. Their behavior was examined after heat treatments at temperatures between 1,100 C and 1,500 C. A possible growth process for alumina grains was induced from the high resolution TEM observation.
焼結過程における高純度α-アルミナ繊維(ALMAX)微構造の発達を解析した。アルミナ粒子の構造は焼結過程で、中間体のδ、γおよびκ相を経て、α相に変化した。SEM(走査型電子顕微鏡)およびTEM(透過型電子顕微鏡)観察では、α相粒子中に多くの気孔が見られた。この気孔生成の挙動を、1,100度Cと1,500度C間の温度における熱処理の後で調べた。アルミナ結晶粒の成長過程を、高分解能TEMにより観察できた。 |
| キーワード | heat treatment; microstructure; alumina fiber; alpha alumina; alumina grain; SEM; scanning electron microscope; TEM; transmission electron microscope; sintering; 熱処理; 微構造; アルミナ繊維; アルファ-アルミナ; アルミナ粒子; SEM; 走査型電子顕微鏡; TEM; 透過型電子顕微鏡; 焼結 |
| 資料種別 | Technical Report |
| ISSN | 0286-0902 |
| SHI-NO | AA0001862007 |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/55191 |