Development of new corrosion resistant stainless steel for sulphuric acid plant

Abstract

New corrosion resistant stainless steel with 6.5 percent silicon and 0.01 percent palladium for use with high temperature sulfuric acid with more than 98 mass percent at high temperatures up to 473 K has been successfully developed in order to get a lighter and smaller structure and realize a heat recovery system. In this study, the effects of the palladium and silicon content on the corrosion resistance of the newly developed steel were clarified. This steel can be easily produced by mill rolling to give an adjustable soaking treatment even when containing more than 6.5 percent silicon. The ductility of welded joints can be maintained by introducing an adjustable ferrite into the microstructure and the welded joint so that sufficient ductility can be provided by TIG (Tungsten Inert Gas arc) welding.

軽量、小型構造の熱回収システムを実現するために、473Kまでの高温下で98質量パーセント以上の高温硫酸向けに6.5パーセントの珪素と0.01パーセントのパラジウムを含有する新耐食性ステンレス鋼を開発した。本研究により新規に開発したステンレス鋼の耐食性に対するパラジウムと珪素含有量の効果を明らかにした。このステンレス鋼は6.5パーセント以上の珪素を含有する場合にも調整均熱処理を行うための圧延により容易に製造が可能である。溶接継手の延性は充分な延性がTIG(タングステン不活性ガスアーク)溶接により与えられる鋼の微細構造への調整可能フェライトの導入および溶接継手により保持できる。