インターカレーション化合物M(x)TiSe2の磁気的性質

Abstract

Polycrystalline samples of intercalation compounds M(x)TiSe2 are prepared, where x = 0.1, 0.2, and Ms are 3d-transition metal elements: V, Cr, Mn, Fe, Co, Ni and Cu. All the samples show paramagnetic behavior. Comparison of this result with the previous result suggests that M-atoms are located in the van der Waals gap between the neighboring Se-layers. The susceptibility data are analyzed to yield effective magnetic moments mu(sub eff). The mu(sub eff) data suggest that all of M strongly hybridize with the TiSe2 band. The electronic states of Cr, Mn, Fe and Co are high-spin states hybridized with the TiSe2 band. By comparing the present data with the calculated band structure and with previous data for M(x)TiS2, mechanisms of the hybridization of the M-band with the TiSe2 band are discussed.

インターカレーション化合物の多結晶試料M(x)TiSe2を作製した。ここで、x=0.1、0.2、Mは3d遷移金属元素(V、Cr、Mn、Fe、Co、Ni、Cu)である。試料はすべて常磁性を示す。この結果と以前の結果を比較すると、M原子は、隣接するSe層間のvan der Waalsギャップ内に配置されているものと思われる。有効磁気モーメントμ(sub eff)を得るため、磁化率データを解析した。μ(sub eff)のデータから、すべてのMはTiSe2バンドと強く混成していることがうかがわれる。Cr、Mn、Fe、Coの電子状態はTiSe2バンドにより混成された高スピン状態である。計算したバンド構造およびM(x)TiSe2に対する以前のデータと今回のデータとを比較することにより、MバンドとTiSe2との混成の機構について検討した。