| タイトル | Materials Characterization of Electron Beam Melted Ti-6Al-4V |
| 本文（外部サイト） | http://hdl.handle.net/2060/20160011332 |
| 著者（英） | Locci, Ivan E.; Martin, Richard E.; Ring, Andrew J.; Telesman, Jack; Garg, Anita; Lerch, Bradley A.; Draper, Susan L. |
| 著者所属（英） | NASA Glenn Research Center |
| 発行日 | 2016-09-01 |
| 言語 | eng |
| 内容記述 | An in-depth material characterization of Electron Beam Melted (EBM) Ti-6Al-4V material has been completed on samples fabricated on an ARCAM A2X EBM machine. The specimens were fabricated under eight separate builds with the material divided into two lots for material testing purposes. Hot Isostatic Pressing (HIP) was utilized to close porosity from fabrication and also served as a material heat treatment to obtain the desired microstructure. The changes in the microstructure and chemistry from the powder to pre-HIP and post-HIP material have been analyzed. Several nondestructive evaluation (NDE) techniques were utilized to characterize the samples both before and after HIP. The test matrix included tensile, high cycle fatigue, low cycle fatigue, fracture toughness, and fatigue crack growth at cryogenic, room, and elevated temperatures. The mechanical properties of the EBM Ti-6Al-4V are compared to conventional Ti-6Al-4V in the annealed condition. Fractography was performed to determine failure initiation site. The EBM Ti-6Al-4V had similar or superior mechanical properties compared to conventionally manufactured Ti-6Al-4V. |
| NASA分類 | Space Sciences (General); Metals and Metallic Materials |
| レポートNO | GRC-E-DAA-TN33083
NASA/TM-2016-219136
E-19261 |
| 権利 | Copyright, Distribution as joint owner in the copyright |
|