| タイトル | Tensile Cyclic Strength and Macroscopic Failure Characteristics of C/C and the Metal Impregnated C/C |
| DOI | info:doi/10.15017/26792 |
| 本文（外部サイト） | https://catalog.lib.kyushu-u.ac.jp/opac_download_md/26792/129_p025.pdf |
| 参考URL | http://hdl.handle.net/2324/26792 |
| 著者（英） | Moriyama, Masahiro; Takao, Yoshihiro; Wang, Wen-Xue; Matsubara, Terutake |
| 発行日 | 2013-08-09 |
| 発行機関など | Research Institute for Applied Mechanics, Kyushu University |
| 刊行物名 | 九州大学応用力学研究所所報 |
| 巻 | 129 |
| 開始ページ | 25 |
| 終了ページ | 30 |
| 刊行年月日 | 2005-09 |
| 言語 | eng |
| 内容記述 | Tensile cyclic strength and macroscopic behavior of C/C and metal impregnated C/C composites such as Cu-C/C and Si-C/C were investigated experimentally. From the results of tensile-tensile cyclic loading tests, S-N curves of these materials were obtained and the fracture mechanism of these materials was discussed. The cyclic strength of metal impregnated C/C composites is about 80% of the ultimate tensile strength at N=10^6. Though strength degradation appears in low cycle region, the residual strength is increased in high cycle region. |
| キーワード | carbon-carbon (C/C); metal impregnated C/C; tensile cyclic loading; S-N curve; Weibull distribution; interface crack; recovery of strength |
| 資料種別 | Departmental Bulletin Paper |