タイトル | Permeation behavior of deuterium implanted into beryllium |
その他のタイトル | ベリリウム中に打ち込まれた重水素の透過挙動 |
DOI | 10.11484/jaeri-research-2001-042 |
本文(外部サイト) | http://jolissrch-inter.tokai-sc.jaea.go.jp/pdfdata/JAERI-Research-2001-042.pdf |
参考URL | http://jolissrch-inter.tokai-sc.jaea.go.jp/search/servlet/search?13906 |
著者(日) | 中村 博文; 林 巧; 大平 茂; 西 正孝 |
発行日 | 2001-09 |
発行機関など | JAEA |
刊行物名 | JAERI-Research 2001-042 |
開始ページ | 1 |
終了ページ | 21 |
刊行年月日 | 2001-09 |
言語 | en |
内容記述 | Study on Implantation Driven Permeation (IDP) behavior of deuterium through pure beryllium was investigated as a part of the research to predict the tritium permeation through the first wall components of ITER (International Thermonuclear Experimental Reactor). The permeation experiments were carried out with two beryllium specimens, one was an unannealed specimen and the other was that annealed at 1173 K. The permeation flux was measured as a function of specimen temperature and incident ion flux. Surface analysis of specimen was also carried out after the permeation experiment. Permeation was observed only with the annealed specimen and no significant permeation was observed with unannealed specimen under the present experimental condition (maximum temperature: 685K, detection limit: 1x1013Datoms/m2s). It could be attributed that the intrinsic lattice defects, which act as diffusion preventing site, decreased with the specimen annealing. Based on the result of steady and transient permeation behavior and surface analysis, it was estimated that the deuterium permeation implanted into annealed beryllium was controlled by surface recombination due to the oxide layer on the surface of the permeated side. 著者所属: 日本原子力研究開発機構(JAEA) |
資料種別 | Technical Report |
URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/617513 |