| タイトル | Toward Optimum Scale and TBC Adhesion on Single Crystal Superalloys |
| 本文（外部サイト） | http://hdl.handle.net/2060/19990027466 |
| 著者（英） | Smialek, James L. |
| 著者所属（英） | NASA Lewis Research Center |
| 発行日 | 1998-01-01
1998 |
| 言語 | eng |
| 内容記述 | Single crystal superalloys exhibit excellent cyclic oxidation resistance if their sulfur content is reduced from typical impurity levels of approximately 5 ppmw to below 0.5 ppmw. Excellent alumina scale adhesion was documented for PWA 1480 and PWA 1484 without yttrium additions. Hydrogen annealing produced effective desulfurization of PWA 1480 to less than 0.2 ppmw and was also used to achieve controlled intermediate levels. The direct relationship between cyclic oxidation behavior and sulfur content was shown. An adhesion criterion was proposed based on the total amount of sulfur available for interfacial segregation, e.g., less than or equal to 0.2 ppmw S will maximize adhesion for a 1 mm thick sample. PWA 1484, melt desulfurized to 0.3 ppmw S, also exhibited excellent cyclic oxidation resistance and encouraging TBC lives (10 mils of 8YSZ, plasma sprayed without a bond coat) in 1100 C cyclic oxidation tests. |
| NASA分類 | Metallic Materials |
| 権利 | No Copyright |
| URI | https://repository.exst.jaxa.jp/dspace/handle/a-is/96639 |
|